VYPET VNT 340 HD
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lavergne Group |
| Trademark: | VYPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3bSWfg_VYPET-VNT-340-HD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vypet VNT 340 HD is a 40% glass/mineral reinforced PET injection molding compound designed for electrical and structural applications, with High Dielectric Strength Features:
Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.64 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 2.00 mm 1 | 0.25 | % | |
| Flow : 3.20 mm 2 | 0.32 | % | |
| Across Flow : 2.00 mm 3 | 0.53 | % | |
| Across Flow : 3.20 mm 4 | 0.79 | % | |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 111 | MPa | ISO 527-2/5 |
| Flexural Modulus 5 | 10500 | MPa | ISO 178 |
| Flexural Stress 6 | 170 | MPa | ISO 178 |
| Compressive Strength 7 | 151 | MPa | ASTM D695 |
| Shear Strength | 59.0 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 6.7 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 224 | °C | ISO 75-2/A |
| Melting Temperature | 249 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.7E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.1E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 8 | ASTM D149 | ||
| 23°C, 1.60 mm, Oil | 22 | kV/mm | |
| 23°C, 3.20 mm, Oil | 16 | kV/mm | |
| Dielectric Constant (1 kHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.011 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 47 | mm/min | ISO 3795 |
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 275 to 300 | °C | |
| Processing (Melt) Temp | 275 to 300 | °C | |
| Mold Temperature | 95.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | (2mmx60mmx60mm) |
| 2 . | (3.2mmx7.6mmx12.6mm) |
| 3 . | (2mmx60mmx60mm) |
| 4 . | (3.2mmx7.6mmx12.6mm) |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 500 V/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam AFR450B1 | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| NaturePlast NP EL 007 | NaturePlast | TPE | NaturePlast |
| Alpha PVC GW 2052 SPEC NAT LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| Lotrène® LDPE FE3000 | QAPCO | LDPE | Lotrène® LDPE |
| LNP™ STAT-KON™ DEL34 compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |