Spartech Polycom EP5140 A1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3auoz7_Spartech-Polycom-EP5140-A1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Talc Filled Extrusion Grade Polypropylene, Natural compound offers a high level of stiffness and heat defection performance balanced with excellent processability. The nominal melt flow of 1.0 g/10min. makes this product ideal for sheet extrusion / thermoforming applications up to 100 mil thickness. A Spartech Polycom representative can provide more information concerning this and other products. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (224°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 34.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | ASTM D638 |
| Fracture | 30 | % | ASTM D638 |
| Flexural Modulus - Secant | 2480 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 0.113 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 79.4 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S RV400K 333 NER | Radici Plastics | Nylon 6 | Radilon® |
| RMA 70 | Ronald Mark Associates, Inc. | PVC Homopolymer | RMA |
| Tarnamid® T-27 GF 25 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Ultramid® A3WG7 | BASF Corporation | Nylon 66 | Ultramid® |
| ADENE NCTEC | A.D. Compound spa | PP Copolymer | ADENE |