Natur-Tec® BF3001J
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | Natur-Tec - Northern Technologies International Corp |
| Trademark: | Natur-Tec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3YZwNm_Natur-Tec-BF3001J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Natur-Tec® BF3001J is a 100% biobased and biodegradable polymer resin compound designed to replace conventional plastic materials for extrusion coating applications. Natur-Tec® BF3001J is manufactured using sustainable and renewable resources, per the ASTM D6866 standard, which allows industry and consumers the opportunity to reduce or neutralize their carbon footprint. Natur-Tec® resins are engineered for high performance and can easily be processed on conventional manufacturing equipment while offering energy savings due to much lower processing temperatures. The BF3001J is designed to meet the requirements of international standards for compostable plastics such as ASTM D6400 (U.S.). Natur-Tec® extrusion coating resins provide good adhesion to paper, an excellent print surface and good heat seal strength. This coating material is suitable for food contact applications including both hot and cold applications. Please refer to the Material Safety Data Sheet and the Processing Guide for specific handling and processing instructions. Natur-Tec® BF3001J can be used for coating paper and paperboards for the manufacture of disposable cups, plates and other food service ware items. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.1 | g/10 min | ASTM D1238 |
| Thickness - Paper board | 230 | g/m² | Internal method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | 1.10 | kgf/25 mm | ASTM D903 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coating Thickness | 30.0 | g/m² | Internal method |
| Renewable Content - (Bio) | 100 | % | ASTM D6866 |
| Resistance to Grease, Fats, and Oils 1 | > 12.0 | Internal method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 12.2 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 10.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 6.0 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 6.8 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 26 | g | ASTM D1922 |
| TD : 25 µm | 24 | g | ASTM D1922 |
| Water Vapor Transmission Rate | 1.3 | g·mm/m²/atm/24 hr | ASTM E398-03 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 66.5 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cobb Test: .2 gm/m² using TAPPI T441 om-90 (2 Min) |
| Note Message | |
|---|---|
| 1 . | 3M test kit, Tappi 559 cm-02 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® G4300HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| ExxonMobil™ LDPE LD 252 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Globalene® HP560P | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| HTA® 512 | Cytec Industries Inc. | MAH-g | HTA® |
| Sylvin 8816-75 GREY 9341 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |