AIE PP 8010HMS-BF02
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3YSWWG_AIEPP8010HMSBF02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Materials Features: It is suitable for hot-plate welding. It has high melt flow stregth and high sag resistance. It can be made into products of semi-transparent, low temperature resistance, impact resistance materials for automotive, motorcycle carbon canister housings, automotive expansion tank, accumulator case, power battery cases and other parts that require for hot-plate welding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.910 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | ASTM D955 |
| Transverse flow | 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | 27.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | > 140 | % | ASTM D638 |
| Flexural Modulus 4 | 800 | MPa | ASTM D790 |
| Flexural Strength 5 | 29.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 74.0 | °C | ASTM D648 |
| Melting Temperature | 166 | °C | DSC |
| CLTE - Flow (-20 to 150°C) | 5.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.10 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1120E | Teknor Apex Company | TPE | Telcar® |
| Vi-Chem PVC V143-70I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Electroblend® HIPS-1802 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PS (HIPS) | Electroblend® |
| Karina CLEAR PVC COMPOUND -E 75/232-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| OmniLon™ PA6/6 U GMR40 BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |