LNP™ STAT-LOY™ KX09024 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3YAzD6_LNP-STAT-LOY-KX09024-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY KX09024 is a compound based on Polyacetal with reduced Resistivity. Added features include: Antistatic Properties Also known as: LNP* STAT-LOY* Compound KX09024 Product reorder name: KX09024 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 2.8 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1000 | MPa | ISO 527-2/1 |
| Tensile Strain (Break) | 12 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 1400 | MPa | ISO 178 |
| Flexural Stress | 48.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 67.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.4E-4 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.6E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+8 to 1.0E+10 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+8 to 1.0E+10 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 188 to 199 | °C | |
| Front Temperature | 199 to 210 | °C | |
| Processing (Melt) Temp | 193 to 204 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-1605 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Topolymer® 6211-P | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Nylene® 5160 HS | Custom Resins Group | Nylon 66 | Nylene® |
| DuraGrip® DGR 6185BK | Advanced Polymer Alloys | TPE | DuraGrip® |
| ESTOPLAST SR 1500GY04 | Ester Industries Ltd. | ABS | ESTOPLAST SR |