SCHULATEC® PEEK GF 30 NV 12
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULATEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3XtcOF_SCHULATEC-PEEK-GF-30-NV-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30 % glass fiber reinforced polyetheretherketone, low viscosity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (400°C/2.16 kg) | 14.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 174 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 10800 | MPa | ISO 178 |
| Flexural Stress 1(3.2% strain) | 286 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 75 | kJ/m² | ISO 179/1eU |
| 23°C | 75 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 68 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 250 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.800 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.60 mm | V-0 | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Rear Temperature | 360 - 370 | °C | |
| Middle Temperature | 380 - 390 | °C | |
| Front Temperature | 390 - 400 | °C | |
| Nozzle Temperature | 360 - 380 | °C | |
| Processing (Melt) Temp | 390 | °C | |
| Mold Temperature | 170 - 190 | °C |
| Note Message | |
|---|---|
| 1 . | At Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® B240MN | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| TECHNYL® A 218 MT15 V25 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| SNOLEN® IM 26/64 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| UNISOFT TPE™ ST-46A-NT-2-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| ANYBES Nylon 12 Fine Powder | SH Energy & Chemical | Nylon 12 | ANYBES |