China PPS hb-DL
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3TyZFG_China-PPS-hb-DL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Low Chlorine type of PPS-hb. It is specially used in E/E industry which requires the chlorine content. PPS-hb is high rigidity crystalline polymer that offers high-temperature resistance, innoxious, flame resistance, radiation resistance, solvent resistance, electrical insulation, arc resistance, low water absorption, low mold shrinkage, good dimensional stability and radiation resistance. It's brittle. Therefore, it needs to be modified by some modifier. Owing to its high performance, it's widely used in medical, electronic/electric industry. Such as: rotproof sealed appliances, plugs, and contactors. It can be modified by different modifiers to make different PPS compounds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) 1(315°C/5.0 kg) | < 100 | g/10 min | Internal method |
| Water Absorption (Saturation) | < 0.50 | % | Internal method |
| Chlorine Content | ppm | Internal method | |
| Molecular weight- Weight Average 2 | > 300000 | ||
| Ash Content | % | Internal method |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Temperature 3 | 340 - 370 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 105 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 300 | °C | |
| Processing (Melt) Temp | 160 - 180 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 60.0 - 70.0 | MPa | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Processing time: 4 to 8hr |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 105 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 160 - 200 | °C | |
| Cylinder Zone 2 Temp. | 260 - 290 | °C | |
| Cylinder Zone 3 Temp. | 280 - 300 | °C | |
| Adapter Temperature | 265 - 275 | °C |
| Extrusion instructions |
|---|
| Degree of vacuum: 0.09 Mpa |
| Note Message | |
|---|---|
| 1 . | 2.095 mm |
| 2 . | Gel Chromatography |
| 3 . | Time: 10~15minPressure: 7~10MpaHeat time: 2~3hrDemoulding temperature: Natural cooling to normal temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 8548V | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Geon™ Vinyl Rigid Extrusion 84110 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| LNP™ LUBRICOMP™ EFL34HL compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| MAXATEL® AH500AL-NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | MAXATEL® |
| Omnix® LF-4050 BK 000 | Solvay Specialty Polymers | HPPA | Omnix® |