LNP™ THERMOCOMP™ DF0046P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3TMYU2_LNP-THERMOCOMP-DF0046P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF0046P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features include: Exceptional Processing, Non-Brominated & Non-Chlorinated Flame Retardant. Also known as: LNP* THERMOCOMP* Compound DF-1004 EP FR ECO Product reorder name: DF0046P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6160 | MPa | ASTM D638 |
| -- | 6930 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 95.1 | MPa | ASTM D638 |
| Break | 97.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.6 | % | ASTM D638 |
| Break | 3.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5980 | MPa | ASTM D790 |
| -- | 6560 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 138 | MPa | ASTM D790 |
| -- | 151 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 2 | 8.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 470 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 10.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 138 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Gallonprene® GP520-7505 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Huaxia Shenzhou FKM DS2601-2 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |
| LUBEMID A26 EL40 NATURAL | LUBEN PLAST srl | Nylon 66 | LUBEMID |
| Polifor® E 12 TR/20 NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
| NORYL™ RN0401 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |