Clearflex® CL D0
| Category: | VLDPE , Very Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3T3BF4_Clearflex-CL-D0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex CL D0 is a linear low density polyethylene, with antioxidants, characterised by a very low density (VLDPE). This resin is produced with a proprietary technology. Stretch films manufactured with Clearflex CL D0 have high stretchability, outstanding clarity and very high constancy in cling effect. Main Application Clearflex CL D0 is recommended as cling agent in stretch film but it is also used for applications in which soft touch and flexibility are required, for the improvement of impact resistance when used as additive in blend with other polyolefins formulated with or without mineral fillers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Cast Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 8 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Cast Film | 40.0 | MPa | |
| 1% Secant, TD : Cast Film | 50.0 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Cast Film | 5.00 | MPa | |
| TD : Yield, Cast Film | 5.00 | MPa | |
| MD : Break, Cast Film | 31.0 | MPa | |
| TD : Break, Cast Film | 26.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Cast Film | 600 | % | |
| TD : Break, Cast Film | 800 | % | |
| Dart Drop Impact 1(Cast Film) | 210 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 40.0 | kN/m | |
| TD | 82.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 54.0 | °C | ISO 306/A |
| Melting Temperature | 115 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Cast Film) | 84 | ASTM D2457 | |
| Haze (Cast Film) | 1.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 270 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PA6 900/8 GF10 MR20 SV1285-04MCF | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| BMC 900 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| GERMAMID 6.6 HXKZNS | Kunststoff-Kontor-Hamburg GmbH | Nylon 66 | GERMAMID |
| Hostaform® S 9364 XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Hylon® N1020L | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |