Durethan® B 31 SK 000000 Datasheet,Nylon 6,LANXESS GmbH-SHANGHAI SUSHENG

Message
PA 6, non-reinforced, injection molding

General Information
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity
--	1.13 1.14	--	g/cm³	ASTM D792
23°C	1.14	--	g/cm³	ISO 1183
Apparent Density	0.60	--	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	110	--	cm³/10min	ISO 1133
Molding Shrinkage				ISO 2577
Across Flow : 280°C, 3.00 mm ¹	1.1	--	%
Across Flow : 120°C, 4 hr, 3.00 mm ²	0.15	--	%
Flow : 280°C, 3.00 mm ³	0.90	--	%
Flow : 120°C, 4 hr, 3.00 mm ⁴	0.15	--	%
Water Absorption				ISO 62
Saturation, 23°C	10	--	%
Equilibrium, 23°C, 50% RH	3.0	--	%

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	150	55.0	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
23°C ⁵	3200	1100	MPa	ASTM D638
23°C	3500	1100	MPa	ISO 527-2/1
Tensile Strength
Yield, 23°C	80.0	40.0	MPa	ASTM D638
Yield, 23°C	85.0	50.0	MPa	ISO 527-2/50
Break, 23°C	50.0	60.0	MPa	ASTM D638
Tensile Elongation
Yield, 23°C	4.0	20	%	ASTM D638, ISO 527-2/50
Break, 23°C	35	> 50	%	ASTM D638
Nominal Tensile Strain at Break (23°C)	10	> 50	%	ISO 527-2/50
Tensile Creep Modulus				ISO 899-1
1 hr	--	900	MPa
1000 hr	--	700	MPa
Flexural Modulus
23°C	2700	703	MPa	ASTM D790
23°C ⁶	3000	900	MPa	ISO 178/A
Flexural Strength
5.0% Strain, 23°C	115	35.0	MPa	ASTM D790
3.5% Strain, 23°C	100	30.0	MPa	ISO 178/A
23°C ⁷	120	40.0	MPa	ISO 178/A
Flexural Strain at Flexural Strength ⁸(23°C)	6.0	8.0	%	ISO 178/A

Flammability	Dry	Conditioned	Unit	Test Method
Burning Behavior ⁹(> 1.00 mm)	passed	--		ISO 3795

Additional Information	Dry	Conditioned		Test Method
ISO Shortname	PA 6, GR, 14-030,	--		ISO 1874

Injection	Dry	Unit	Test Method
Residual Moisture Content	0.030 to 0.12	%	Karl Fisher

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-40°C	< 10	< 10	kJ/m²
-30°C	< 10	< 10	kJ/m²
23°C	< 10	25	kJ/m²
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	No Break	No Break
23°C	No Break	No Break
Notched Izod Impact
23°C, 3.18 mm	59	750	J/m	ASTM D256
-30°C	< 10	< 10	kJ/m²	ISO 180/1A
23°C	< 10	< 10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength				ISO 180/1U
-30°C	120	--	kJ/m²
23°C	120 kJ/m²	No Break
Multi-Axial Instrumented Impact Energy				ISO 6603-2
-30°C	70.0	--	J
23°C	46.0	--	J
Multi-Axial Instrumented Impact Peak Force				ISO 6603-2
-30°C	6810	--	N
23°C	4650	--	N

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed, 39.9 mm	180	--	°C	ASTM D648
0.45 MPa, Unannealed	170	--	°C	ISO 75-2/B
1.8 MPa, Unannealed	60.0	--	°C	ISO 75-2/A
1.8 MPa, Annealed, 3.99 mm	60.0	--	°C	ASTM D648
8.0 MPa, Unannealed	50.0	--	°C	ISO 75-2/C
Vicat Softening Temperature	200	--	°C	ISO 306/B50, ISO 306/B120
Melting Temperature ¹⁰	222	--	°C	ISO 11357-3
CLTE				ISO 11359-2
Flow : 23 to 55°C	7.0E-5	--	cm/cm/°C
Transverse : 23 to 55°C	9.0E-5	--	cm/cm/°C
RTI Elec (1.50 mm)	105	--	°C	UL 746
RTI Imp (1.50 mm)	65.0	--	°C	UL 746
RTI Str (1.50 mm)	75.0	--	°C	UL 746

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+13 to 1.0E+15	1.0E+12 to 1.0E+14	ohms	IEC 60093
Volume Resistivity (23°C)	1.0E+15	1.0E+12	ohms·cm	IEC 60093
Electric Strength				IEC 60243-1
23°C, 1.00 mm	30	30	kV/mm
23°C, 3.00 mm	30	35	kV/mm
Dielectric Constant				IEC 60250
23°C, 50 Hz ¹¹	3.80	20.0
23°C, 1 MHz ¹²	3.40	4.60
23°C, 100 Hz	4.00	13.0
23°C, 1 MHz	3.50	4.00
Dissipation Factor				IEC 60250
23°C, 50 Hz	0.050	2.3
23°C, 100 Hz	6.0E-3	0.19
23°C, 1 MHz	0.020 0.070	0.10 0.40
Comparative Tracking Index
Solution A	600	--	V	IEC 60112
Solution B	450 525	--	V	IEC 60112
--	--	600	V	ASTM D3638

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
1.50 mm	V-2	--
1.60 mm	V-2	--
3.00 mm	V-2	--
3.20 mm	V-2	--
Glow Wire Flammability Index (2.00 mm)	750	--	°C	IEC 60695-2-12
Oxygen Index ¹³	25	--	%	ISO 4589-2

Injection	Dry	Unit
Drying Temperature - Dry Air Dryer	80.0	°C
Drying Time - Dry Air Dryer	2.0 to 6.0	hr
Processing (Melt) Temp	260 to 280	°C
Mold Temperature	80.0 to 100	°C

Category:	Nylon 6 , Polyamide 6
Manufacturer:	LANXESS GmbH
Trademark:	Durethan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3Swe0p_Durethan-B-31-SK-000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Premi-Glas® 2208-CR-SX	Premix, Inc.	TS, Unspecified	Premi-Glas®
SCANAMID 66 A53^E	Polykemi AB	Nylon 66	SCANAMID 66
Celanex® 3216	Celanese Corporation	PBT	Celanex®
Ebalta MG 815 / Comp. A+B	Ebalta Kunststoff GmbH	PUR, Unspecified	Ebalta
Hanwha Total PP FB53	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, Unspecified	Hanwha Total PP