LubriOne™ 5209 FPL 20 Natural
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3Rqhgr_LubriOne-5209-FPL-20-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 2.0 to 3.0 | % | |
| Across Flow | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2420 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 42.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 26 | % | ASTM D638 |
| Flexural Modulus 4 | 1790 | MPa | ASTM D790 |
| Flexural Strength 5 | 68.3 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.12 | ||
| vs. Steel - Static | 0.13 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 37 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 153 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 82.8 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Compound 822 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Edgetek™ SF-30GF/000 NC005 | PolyOne Corporation | PPS | Edgetek™ |
| Electrafil® PA6/6 C BK | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| Kumho SBR 1507H | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| POCAN® T 7391 000000 | LANXESS GmbH | PBT+PET | POCAN® |