PROTEQ™ C12UST4Z
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3QEGHT_PROTEQ-C12UST4Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PROTEQ™ C12UST4Z is a super tough, 20% talc filled polypropylene copolymer which features ultra high impact strength at sub zero temperatures together with improved heat ageing and UV performance. PROTEQ™ C12UST4Z has been designed to meet the stringent requirements of automotive interior trim durability specifications, combining easy processing with reduced gloss and improved marr resistance. Typical applications are interior trim mouldings adjacent to or surrounding airbags. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 64 | ||
| Shore D, 15 sec | 55 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| 3.20 mm 1 | 17.0 | MPa | |
| 3.20 mm 2 | 20.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, 3.20 mm 3 | 580 | % | |
| Break, 3.20 mm 4 | 250 | % | |
| Flexural Modulus | ASTM D790 | ||
| 3.20 mm 5 | 1350 | MPa | |
| 3.20 mm 6 | 1650 | MPa | |
| Flexural Strength | ASTM D790 | ||
| 3.20 mm 7 | 27.0 | MPa | |
| 3.20 mm 8 | 32.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 380 | J/m | |
| 0°C, 3.20 mm | 530 | J/m | |
| 23°C, 3.20 mm | 630 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 118 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 60.0 | °C | |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 195 to 215 | °C | |
| Middle Temperature | 205 to 225 | °C | |
| Front Temperature | 215 to 235 | °C | |
| Processing (Melt) Temp | 220 to 270 | °C | |
| Mold Temperature | 30.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 10 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tectron H2406 | TECTRON Systems Pte Ltd | TPV | Tectron |
| Axiall PVC 7181 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| ELASTICHEM™ 7011TX-02 | Colorite Polymers | PVC, Flexible | ELASTICHEM™ |
| HiFill® PET GF30 2000 | Techmer Engineered Solutions | PET | HiFill® |
| KRATON® G2832 GS-N | Kraton Polymers LLC | SEBS | KRATON® |