BESTNYL SE15VI02AS16
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3PX1i0_BESTNYL-SE15VI02AS16.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6,6 black lubrified with 15% glass fibre reinforcement and 25% of mineral charge, is ideal for final applications in the need of good mechanical characteristics and high dimensional stability, generally used in interior pieces in automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ISO 62 |
| Ash Content | 40 | % | Internal Method |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2 |
| Tensile Stress | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Electric Strength | 35 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Processing (Melt) Temp | 275 to 285 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Arlon® 1163 | Greene, Tweed & Co. | PEEK | Arlon® |
| Chemiton TGB2NA 30 | Franplast S.r.l. | SEBS | Chemiton |
| ColorRx® PP1-6000RX | LTL Color Compounders, Inc. | PP Homopolymer | ColorRx® |
| LNP™ LUBRILOY™ K2000 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRILOY™ |
| POLYabs R00 | Polykemi AB | ABS | POLYabs |