HiPrene® HLG73BBE
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GS Caltex |
| Trademark: | HiPrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3OTIOd_HiPrene-HLG73BBE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiPrene® HLG73BBE is polypropylene with 30% long glass fibers-blended type with impact copolymer. This material combines excellent strength and stiffness with perfect impact resistance at low temperatures also. This grade is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Ash Content (600°C) | 30 | % | ISO 3451 |
| Volatile Matter | 0.12 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 5200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 24 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 156 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 240 to 250 | °C | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 30.0 to 75.0 | °C | |
| Injection Pressure | 55.0 to 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 40.0 to 80.0 | MPa | |
| Back Pressure | 0.00 to 3.00 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 685 | RTP Company | ABS | RTP |
| Moplen PPU 1752HL23 | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Borealis PP HC600TF | Borealis AG | PP Homopolymer | Borealis PP |
| Halar® 7114 | Solvay Specialty Polymers | ECTFE | Halar® |
| Hanwha Total PP GB14 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |