Estane® 2103-80PF TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3MU5Ub_Estane-2103-80PF-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
2103-80PF is a thermoplastic polyurethane elastomer. Feature: Film and profile resin |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/8.7 kg) | 39 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 1.60 mm | -0.20 to 0.50 | % | |
| Across Flow : 1.60 mm | 0.40 to 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 to 88 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 5.00 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 50% Strain | 4.10 | MPa | |
| 100% Strain | 5.20 | MPa | |
| 300% Strain | 7.90 | MPa | |
| Tensile Strength (Break) | 26.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 660 | % | ASTM D412 |
| Elongation Set After Break | 50 | % | ASTM D412 |
| Tear Strength 1 | 78.8 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 25°C, 22 hr | 25 | % | |
| 70°C, 22 hr | 80 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -46.0 | °C | DSC |
| Vicat Softening Temperature | 68.9 | °C | ASTM D1525 |
| CLTE - Flow | 1.7E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.0 to 93.0 | °C | |
| Processing (Melt) Temp | 188 to 204 | °C | |
| Mold Temperature | 16.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.0 to 93.0 | °C | |
| Melt Temperature | 182 to 199 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® M-687 | Matrix Polymers | Plastomer | REVOLVE® |
| TEKNIFLEX® VPOA12200 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| Vi-Chem PVC VDM93-30E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Akulon® K222-KGV4 /A | DSM Engineering Plastics | Nylon 6 | Akulon® |
| HiFill® PA6 0325 | Techmer Engineered Solutions | Nylon 6 | HiFill® |