Bergamid™ X BG6600-8048 RS HS NC001

Category: Nylon 66 , Polyamide 66
Manufacturer: PolyOne Corporation
Trademark: Bergamid™
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: 3M3PSu_Bergamid-X-BG6600-8048-RS-HS-NC001.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Glass Fiber Reinforced PA66 Compound with Heat Stabilized
General Information
Filler / Reinforcement
  • Glass fiber reinforced material, 15% filler by weight
Appearance
  • Natural color
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Density 1.25g/cm³ISO 1183
Molding Shrinkage 0.60 - 1.0%ASTM D955
MechanicalNominal ValueUnitTest Method
Tensile Stress 130MPaISO 527-2
Flexural Modulus 5000MPaISO 178
Flexural Stress 180MPaISO 178
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength 6.0kJ/m²ISO 179
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm)230°CASTM D648
FlammabilityNominal ValueTest Method
Flame Rating (1.60 mm)HBInternal method
InjectionNominal ValueUnit
Drying Temperature 80.0 - 90.0°C
Drying Time 4.0 - 6.0hr
Rear Temperature 260 - 280°C
Middle Temperature 260 - 280°C
Front Temperature 260 - 280°C
Mold Temperature 65.0 - 85.0°C
Injection instructions
Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW
Resin Grade Manufacturer Category Trademark
RTP 600 FR AB RTP Company ABS RTP
Spartech Polycom F5134T4-1 Spartech Polycom PP, Unspecified Spartech
DJSilicone NE-5130 DONGJUE SILICONE (NANJING) CO., LTD Silicone DJSilicone
Fainplast PVC RKI 01298/W-UV Fainplast Compounds S.r.l PVC, Rigid Fainplast PVC
Laprene® 83B000956 SO.F.TER. SPA SEBS Laprene®