HiFill® PP GF20 CC LE
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3LKhgV_HiFill-PP-GF20-CC-LE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PP GF20 CC LE is a Polypropylene product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. Typical application: Food Contact Applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4310 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 163 | °C | |
| 1.8 MPa, Unannealed | 154 | °C | |
| Melting Temperature | 163 | °C | |
| CLTE - Flow | 3.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 21 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 805 HB | RTP Company | Acetal (POM) Copolymer | RTP |
| Stirolan DF AE V0 1.6 | Soredi S.p.a. | PS (HIPS) | Stirolan |
| CGPC PVC R-11X HI Extrusion | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| DESLON™ 66 DSC201FR | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| WELLAMID Nylon 6600-PA66-GV 25 HWV0CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |