| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | KMI Group, Inc. |
| Trademark: | Nylux |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3K2y7v_Nylux66NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylux66-NAT is a general purpose PA66 grade well suited for injection molding and extrusion applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow : 2.00mm | 1.8 | % | ISO 294-4 |
| Flow : 2.00mm | 1.9 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.4 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 82.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.2 | % | ISO 527-2 |
| Fracture | 50 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact (23°C) | 5.4 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 204 | °C | |
| Melting Temperature | 261 | °C | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 4.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aaroprene® CFPP 2010 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
| ALTECH® NXT PP-H A 2030/457 HH GF30 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® NXT PP-H |
| Generic Acetal (POM) Copolymer - Aramid Fiber | Generic | Acetal (POM) Copolymer | Generic |
| Karina GRAY PVC COMPOUND -E 828-18/569-Y-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polaris™ C 80355-13 UV | Ashland Performance Materials | Polyester, TS | Polaris™ |