VECTRA® E130i
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3IAgGE_VECTRA-E130i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High temperature capability, easiest flow. Suitable where very thin walls are required. Used for broad range of SMT applications, with minimal dimensional change. 30% glass filled. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant FDA compliant UL-Listing V-0 in natural and black at .2mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electrical 240°C, mechanical 240°C at 0.75mm. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.40 | % | ISO 294-4 |
| Flow direction | 0.10 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.030 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 71 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.6 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 13500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 220 | MPa | ISO 178 |
| Compressive Modulus | 14000 | MPa | ISO 604 |
| Compressive Stress (1% Strain) | 93.0 | MPa | ISO 604 |
| Flexural Strain at Break | 2.2 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 43 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 31 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 276 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 216 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 195 | °C | ISO 306/B50 |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 7.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | kV/mm | IEC 60243-1 |
| Relative Permittivity | |||
| 100 Hz | 4.00 | IEC 60250 | |
| 1 MHz | 3.30 | IEC 60250 | |
| 2.05 GHz | 4.23 | Internal method | |
| Dissipation Factor | |||
| 100 Hz | 0.010 | IEC 60250 | |
| 1 MHz | 0.025 | IEC 60250 | |
| 2.05 GHz | 6.0E-3 | Internal method | |
| Arc Resistance | 140 | sec | Internal method |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index | 45 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 170 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 315 - 325 | °C | |
| Middle Temperature | 320 - 330 | °C | |
| Front Temperature | 325 - 335 | °C | |
| Nozzle Temperature | 335 - 345 | °C | |
| Processing (Melt) Temp | 335 - 345 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 335 to 345°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP2151 | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Thermec™ 4150CF20 | Technical Polymers, LLC | PPS | Thermec™ |
| TRANSMARE® 19HT40-0.002 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| Bapolene® LL3039 BLK | Bamberger Polymers, Inc. | LLDPE | Bapolene® |
| PLUSTEK RA353M8 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |