Alkathene® Ultra LDD203
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkathene® Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3HR2cX_Alkathene-Ultra-LDD203.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDD203 is a low density polyethylene designed for a variety of medium to heavy gauge (50-150µm) general purpose film applications. LDD203 is formulated with a process stabilisation and antiblock additive package but contains no slip additives. LDD203 is intended for use in a medium to heavy gauge (50-150µm) general purpose film applications and blending into other film grades. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.45 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 50 µm, blown film | 160 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm, blown film | 190 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 26.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 330 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 730 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 370 | g | ASTM D1922 |
| TD : 50 µm, blown film | 250 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 62 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from blown film processed at a blow up ratio of 2:1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIEL® HV5401BH | Samyang Corporation | TPEE | TRIEL® |
| ALTECH® PA6 C 2035/507 GF35 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| DENKA EVA TEX 70 | Denka Company Limited | EVA | DENKA EVA TEX |
| DuraFlex 717 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraFlex |
| LG ABS AF312A | LG Chem Ltd. | ABS | LG ABS |