Infino WR-7390
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3HPozE_InfinoWR7390.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino WR-7390 is an acrylonitrile-styrene-acrylate PC (ASA PC) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 32 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.50 - 0.90 | % | ASTM D955 |
| Traffic : 3.20mm | 0.50 - 0.90 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 118 | ASTM D785 | |
| R scale | 116 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2100 | MPa | ASTM D638 |
| -- | 2120 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 54.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 65.0 | MPa | ASTM D638 |
| Fracture | 61.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 110 | % | ASTM D638 |
| Fracture | 90 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2400 | MPa | ASTM D790 |
| -- 6 | 2140 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 78.0 | MPa | ASTM D790 |
| -- 8 | 84.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 56 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 650 | J/m | ASTM D256 |
| 23°C 10 | 40 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 127 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 112 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 111 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 134 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Hot air dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 | hr | |
| Hot air dryer | 4.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.070 | % | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 60 | °C | |
| Injection Pressure | 93.0 | MPa | |
| Back Pressure | 0.500 | MPa | |
| Screw Speed | 50 | rpm |
| Injection instructions |
|---|
| Hot Runner Manifold Temperature: 280°CHot Runner Valve Nozzle Temperature: 280°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1000 HI FR A | RTP Company | PBT | RTP |
| ALCOM® PC 740/4 UV WT1445-06LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Durez® 33681 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| FRblend® PP-1503 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP, Unspecified | FRblend® |
| SQUARE® LSR6900-20A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |