MBA PP 2172
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | MBA Polymers |
| Trademark: | MBA PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3HIGdI_MBA-PP-2172.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A post-consumer recycled polypropylene copolymer with a high melt flow rate for injection moulding applications. Available in standard black (reference 90/04). |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 18.0 | MPa | ISO 527-2/50 |
| Flexural Modulus (23°C) | 900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 49.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 136 | °C | ISO 306/A50 |
| -- | 58.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Melt Temperature | 180 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sultron® 70C4 | Asia International Enterprise (Hong Kong) Limited | PPS | Sultron® |
| EPO-TEK® 377 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| HiFill® PBT 1225 LE | Techmer Engineered Solutions | PBT | HiFill® |
| K PP 9072 AP | Technovinyl Polymers India Ltd. | PP, Unspecified | K PP |
| POCAN® KU 1-7635 POS 151 000000 | LANXESS GmbH | PC+PBT | POCAN® |