Hanwha Total PP SI73
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3G6tdi_Hanwha-Total-PP-SI73.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SI73 is a high gloss polypropylene compound with improved heat resistance. This product has the high heat-resistance required for use in electric heating equipment parts, as well as superior surface gloss and scratch-resistance. SI73 is one of Korea's best high heat-resistant, high glossy compound products. SI73 is designed for the exterior housings of household appliances which require an elegant appearance, such as rice cookers, toasters, irons, jars, pots, and bread makers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.2 - 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 37.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 60 | % | ASTM D638 |
| Flexural Modulus 3 | 2400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 138 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 180 - 210 | °C | |
| Nozzle Temperature | 180 - 210 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Injection Pressure | 39.2 - 68.6 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa |
| Injection instructions |
|---|
| Injection Speed: 40 to 70 % |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® A60K6 NAT001 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| Clear Cote™ POLY-U-FOAM™ 2 lb Urethane Foam System | Club Kit, Inc. | PUR, Unspecified | Clear Cote™ |
| Grivory® GVX-65 H nat | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Karina BLACK PVC COMPOUND 70900-48/1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAXAMID™ RC66M40HSL-BK09 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |