Shin-Etsu Elastomer KEG-2000-30A/B
| Category: | Silicone Rubber, HTV , Silicone Rubber, HTV |
| Manufacturer: | Shin-Etsu Silicones of America |
| Trademark: | Shin-Etsu Elastomer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3DW9VU_Shin-Etsu-Elastomer-KEG-2000-30A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Shin-Etsu KEG-2000-30 is a liquid injection molding silicone. It is supplied as two components which are mixed in a 1:1 ratio to ensure easy and accurate blending. The viscosity of KEG-2000-30 is low enough to allow easy pumping through most injection molding systems.
Typical Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness | 32 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Stress (100% Strain) | 0.703 | MPa | |
| Tensile Strength | 8.50 | MPa | |
| Tensile Elongation (Break) | 750 | % | |
| Tear Strength 1 | 25.0 | kN/m | |
| Compression Set (180°C, 22 hr) | 6.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life (32°C) | 26 | wk | |
| Post Cure Time (200°C) | 4.0 | hr |
| Additional Information |
|---|
| Press / Post Cure: Press/Post |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time | 0.083 | hr |
| Note Message | |
|---|---|
| 1 . | B mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil R-1400 | NuSil Technology | Silicone | NuSil |
| Nypol® PA B3 G10 V10 NTLA010 NT309 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| KER® 1500 | Synthos S.A. | SBR, Emulsion | KER® |
| Kotex K-20UV | Kotec Corporation | PC | Kotex |
| INNOMID® CS 6-9830 HD | Inno-Comp Ltd. | Nylon 6 Alloy | INNOMID® |