UNITHENE® LH606

Category:	HDPE , High Density Polyethylene
Manufacturer:	USI Corporation
Trademark:	UNITHENE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3BfdTV_UNITHENE-LH606.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

UNITHENE LH606 is a high density polyethylene (HDPE) suitably used for injection molding and filament applications. Typical applications are the injection molding of fruit crates, food containers, industrial items such as pallets, transportation crates, housewares, toys and the fine filament extrusion of mosquito nets.
UNITHENE LH606 possesses high impact strength and good resistance to stress cracking, good stiffness, high hardness, good surface gloss, less warpage, low shrinkage.
UNITHENE LH606 can be easily pigmented to any color by either dry blending or melt blending of the pigment into the resin. Printing on items molded from UNITHENE LH606 can be easily accomplished after a simple flame, chemical or electronic surface treatment.

General Information
Features	Low warpage Rigid, good High ESCR (Stress Cracking Resistance) High density Gloss, Medium Impact resistance, high Workability, good Compliance of Food Exposure Low shrinkage High hardness Excellent appearance
Uses	monofilament Non-specific food applications Industrial application Household goods Agricultural application Food container Toys Web Loading box
Processing Method	Filament extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.962	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)	6.0	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	69		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus - 1% Secant (Compression Molded)	971	MPa	ASTM D638
Tensile Strength			ASTM D638
Yield	30.4	MPa	ASTM D638
Fracture	21.6	MPa	ASTM D638
Tensile Elongation (Break)	600	%	ASTM D638
Apparent Bending Modulus	971	MPa	ASTM D747

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	69	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746
Vicat Softening Temperature	127	°C	ASTM D1525
Peak Melting Temperature	135	°C	ASTM D3418

Additional Information
Torsional Stiffness, ASTM D1043: 12500 kg/cm²

Resin Grade	Manufacturer	Category	Trademark
SUMILITE® CEL-9200	Sumitomo Bakelite Co., Ltd.	LLDPE	SUMILITE®
Toughblend® PBT-1400	Colour Image Plastic Compound Sdn. Bhd. (CIPC)	PBT	Toughblend®
KYOCERA KE-200DC-1	KYOCERA Chemical Corporation	Epoxy	KYOCERA
Lucofin® 1400SL	Lucobit AG	EBA	Lucofin®
Sylvin 8260-65FUV Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin