LNP™ LUBRICOMP™ DL001 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3B6yWs_LNP-LUBRICOMP-DL001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DL001 is a compound based on Polycarbonate resin containing 5% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DL-4010 Product reorder name: DL001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.90 to 1.1 | % | ASTM D955 |
| Across Flow : 24 hr | 0.96 | % | ISO 294-4 |
| Flow : 24 hr | 0.78 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2190 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 56.5 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2 |
| Break | 51.7 | MPa | ASTM D638 |
| Break | 53.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.2 | % | ASTM D638 |
| Yield | 6.1 | % | ISO 527-2 |
| Break | 77 | % | ASTM D638 |
| Break | 170 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2100 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.39 | ||
| vs. Itself - Static | 0.32 | ||
| Wear Factor - Washer | 91.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| 23°C 2 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2400 | J/m | ASTM D4812 |
| 23°C 3 | 180 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 39.6 | J | ASTM D3763 |
| -- | 49.4 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 142 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 142 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 132 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 129 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| LEXAN™ HFR1724 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| POTICON PW36 | Otsuka Chemical Co., Ltd. | PP, Unspecified | POTICON |
| TOTAL Polypropylene PPH 3274 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Sylvin 5132-86 Clear Yellow 4174 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 2989-66D White 1581 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |