TECHNYL® C 548B V15 BLACK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 392QIX_TECHNYL-C-548B-V15-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECHNYL®C 548B V15 BLACK is a polyamide 6 (nylon 6) material, which contains a 15% glass fiber reinforced material. This product is available in North America or Asia Pacific region. The processing method is extrusion blow molding. TECHNYL®The main features of C 548B V15 BLACK are:
TECHNYL®The typical application field of C 548B V15 BLACK is: automobile industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5000 | 3800 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 85.0 | 70.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.0 | 5.0 | % | ISO 527-2/1A |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 14 | 22 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 185 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 4.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength | -- | 21 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.12 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Cylinder Zone 1 Temp. | 210 - 230 | °C | |
| Cylinder Zone 3 Temp. | 230 - 250 | °C | |
| Cylinder Zone 5 Temp. | 240 - 255 | °C | |
| Die Temperature | 250 - 255 | °C |
| Extrusion instructions |
|---|
| Accumulator: 240 to 250°CMold Temperature: 60 to 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HMP-307M (Roto) | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| Network Polymers PP PPH 30 1200 TF40 | Network Polymers, Inc. | PP Homopolymer | Network Polymers PP |
| Flontech® FT-GL3-3 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| PETILEN MH 318 | PETKIM Petrokimya Holding A.S. | PP, Unspecified | PETILEN |
| Moplen HP601N | PolyMirae | PP Homopolymer | Moplen |