SABIC® HDPE PCG80063
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 37q84F_SABIC-HDPE-PCG80063.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG80063 is designed for the injection moulding of healthcare packaging, caps and closures and other parts for medical packaging. It is an easy-to-process, stiff grade. SABIC® HDPE PCG80063 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.963 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 8.0 | g/10 min | |
| 190°C/5.0 kg | 23 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 11.0 | cm³/10min | |
| 190°C/5.0 kg | 30.0 | cm³/10min | |
| Environmental Stress-Cracking Resistance 1(60°C, 3.00 mm, Rhodacal-DS10) | 40.0 | hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1450 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 31.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 15.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 200 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 625 | MPa | |
| 1000 hr | 275 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Compression Molded | 4.0 | kJ/m² | |
| 23°C, Compression Molded | 4.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 94.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 129 | °C | ISO 306/A |
| Melting Temperature (DSC) | 134 | °C | DIN 53765 |
| Enthalpy Change | 226 | J/g | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8210-85C White 1487 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NYCOA Polyamide 6115 HS | Nycoa (Nylon Corporation of America) | Nylon 612 | NYCOA Polyamide |
| Borclear™ RC737MO | Borealis AG | PP Random Copolymer | Borclear™ |
| MAJORIS GFRH300 | AD majoris | PP, Unspecified | MAJORIS |
| Wuxi Jiahong EB-2022 | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |