INTEGRAL™ D202
| Category: | Polyolefin, Unspecified , Polyolefin Adhesive Film |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INTEGRAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3774a9_INTEGRAL-D202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INTEGRAL D202™ film is used as a lamination film. One side provides release separator properties in applications that require a protective sheet that must release from a surface. The other side provides excellent adhesion to substrates such as polyethylene, metal, glass and nylon and has excellent optics. Please discuss your particular application needs with your Dow representative. General Characteristics:
|
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 76 | µm | ASTM D374 |
| Film Thickness - Recommended / Available | 3 mil (76 µm) | ||
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 76 µm | 190 | MPa | |
| 2% Secant, TD : 76 µm | 180 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 76 µm | 36.0 | MPa | |
| TD : Yield, 76 µm | 33.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 76 µm | 280 | % | |
| TD : Break, 76 µm | 320 | % | |
| Film Width | 127.00 to 193.04 | cm | |
| Yield (76.2 µm) | 13.8 | m²/kg | ASTM D4321 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4780 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RAMOFIN PPC371B73 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| Exxtral™ Performance Polyolefin CMU236 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Karina BLACK PVC COMPOUND 105900-48/1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PONACOM PS 5480 | Ponachem Compound GmbH | PS (HIPS) | PONACOM PS |