Adflex KS311P
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 35NUDR_Adflex-KS311P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adflex KS311P is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is suitable for extrusion as well as injection molding and blow molding applications, including mechanical and decorative automotive parts requiring elastomeric type properties, like molded-in color automotive exterior components. The product is in fact used by our customers for applications with paintable and weatherable requirements, such as injection molded fascias, claddings, bumper covers, body panels, step pads, and air deflectors. It is also used as a component in compounded materials for a wide range of industrial applications. The grade is available in natural pellet form. For regulatory compliance information see Adflex KS311P Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 46 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 14.0 | MPa | |
| Break, 23°C | 19.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 14 | % | |
| Break, 23°C | > 800 | % | |
| Flexural Modulus - Chord 1(23°C) | 530 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 103 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C, Partial Break | 4.0 | kJ/m² | |
| 23°C, Partial Break | 49 | kJ/m² | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, 3.20 mm, Energy at Peak Load, Ductile Failure 3 | 26.0 | J | |
| 23°C, 3.20 mm, Energy at Peak Load, Ductile Failure 4 | 14.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 55.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 112 | °C | ISO 306/A50 |
| Melting Temperature | 147 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Die C, 50 mm/min |
| 3 . | 6.60 m/sec |
| 4 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ W600B | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| TYNEC® CG100 | Tyne Plastics LLC. | PC | TYNEC® |
| Favorite REG200 | Favorite Plastics | PE, Unspecified | Favorite |
| EL-Lene™ H5211PYL | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| Iupital® FX-11 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |