Elastollan® 1264 D 13 U 000
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 35MRDm_Elastollan1264D13U000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High transparent, thermoplastic Polyether-Polyurethane with outstanding hydrolysis resistance, low temperature flexibility and high resistance to micro-organisms. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 3 sec) | 64 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 310 | MPa | ISO 527-2 |
| Abrasion Loss | 40.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 17.0 | MPa | DIN 53504-S2 |
| 100% strain | 25.0 | MPa | DIN 53504-S2 |
| 300% strain | 35.0 | MPa | DIN 53504-S2 |
| Tensile Stress (Yield) | 50.0 | MPa | DIN 53504-S2 |
| Tensile Elongation (Break) | 350 | % | DIN 53504-S2 |
| Tear Strength 1 | 170 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 48 | % | ISO 815 |
| 70°C, 24 hr | 48 | % | ISO 815 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 12 | kJ/m² | ISO 179 |
| 23°C | No Break | ISO 179 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 110 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 | °C | |
| Rear Temperature | 200 - 230 | °C | |
| Middle Temperature | 205 - 240 | °C | |
| Front Temperature | 210 - 240 | °C | |
| Nozzle Temperature | 220 - 250 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 15 - 70 | °C | |
| Injection Rate | Slow |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 175 - 195 | °C | |
| Cylinder Zone 2 Temp. | 185 - 205 | °C | |
| Cylinder Zone 3 Temp. | 200 - 220 | °C | |
| Cylinder Zone 4 Temp. | 205 - 215 | °C | |
| Adapter Temperature | 220 - 240 | °C | |
| Die Temperature | 210 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POOYATAK CG203 | Pooya Polymer Tehran | PE, Unspecified | POOYATAK |
| UBE Polyethylene R500 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Braskem PE SLH0820/30AF | Braskem | LLDPE | Braskem PE |
| ColorRx® PE2-4000RX | LTL Color Compounders, Inc. | HDPE | ColorRx® |
| Durethan® B 30 S 000000 | LANXESS Corporation | Nylon 6 | Durethan® |