TECHNO ABS F5451G30
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | TECHNO ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 35Hrvl_TECHNO-ABS-F5451G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECHNO ABS F5451G30 is an Acrylonitrile Butadiene Styrene (ABS) product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.10 to 0.30 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 113 | ASTM D785 | |
| R-Scale | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 98.1 | MPa | ASTM D638 |
| Yield | 91.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8040 | MPa | ASTM D790 |
| -- | 7260 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 128 | MPa | ASTM D790 |
| -- | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 102 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.10 mm, ALL | V-0 | ||
| 2.50 mm, ALL | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 180 to 230 | °C | |
| Middle Temperature | 180 to 230 | °C | |
| Front Temperature | 180 to 230 | °C | |
| Mold Temperature | 50.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Celstran® PA66-GF50-02 P11 | Celanese Corporation | Nylon 66 | Celstran® |
| Clariant Nylon 6 60G33-L | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| InSphere® 1640F | Synthos S.A. | PS (EPS) | InSphere® |
| ISPLEN® PR 264 M1F | REPSOL | PP Random Copolymer | ISPLEN® |
| LNP™ THERMOCOMP™ HF008 compound | SABIC Innovative Plastics | Nylon 11 | LNP™ THERMOCOMP™ |