Clear-Flex® FG 106 A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clear-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 34CZC3_ClearFlexFG106A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex FG 106 A is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion. Film manufactured with Clearflex FG 106 A are characterised by excellent optical properties (haze and gloss), optimum sealing performances and high mechanical properties. Main Applications Clearflex FG 106 A thanks to high purity and low diffusivity of the additives, is particularly suitable in applications such as food packaging. Clearflex FG 106 A is recommended for the production of agricultural film, blown stretch film coextruded or blended with LDPE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% secant, MD : 25 µm, blown film | 180 | MPa | ISO 527-3 |
| 1% secant, TD : 25 µm, blown film | 210 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, blown film | 9.00 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, blown film | 10.0 | MPa | ISO 527-3 |
| MD : Broken, 25 µm, blown film | 50.0 | MPa | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 45.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 25 µm, blown film | 600 | % | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 700 | % | ISO 527-3 |
| Dart Drop Impact (25 µm, Blown Film) | 160 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 25.0 µm | 130.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 230.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 101 | °C | ISO 306/A |
| Melting Temperature | 125 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 10 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITIKA Nylon 6 EX-8406G30 | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| Ferro PP TPP40AA05NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| EMOPLEN® HP MTF 10 | EMAS Plastik San.Tic.AS. | PP Homopolymer | EMOPLEN® |
| MAJORIS EE097 - 7803 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 4212-88UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |