Hostacom HKC 465T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 33qTfB_Hostacom-HKC-465T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" HKC 465T is a 20 % mineral filled polypropylene homopolymer containing post industrial scrap. It combines a good flowability with a high stiffness. The grade has been specifically designed for non visible and not colour matched structural IT and duct parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 12 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 10 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 23.0 | MPa | ASTM D638 |
| Flexural Modulus | |||
| -- | 2200 | MPa | ASTM D790 |
| Secant : 23°C | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 35 | J/m | ASTM D256 |
| 23°C | 2.5 | kJ/m² | ISO 180/1A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS Reprocessed PPC 30/2 RBK | Nexus Resin Group, LLC. | PP Copolymer | NEXUS Reprocessed |
| AEI SX-0620:CM601 | AEI Compounds Limited | XLPE | AEI |
| Bynel® 4157 | DuPont Packaging & Industrial Polymers | LLDPE | Bynel® |
| LNP™ LUBRICOMP™ UX06427 compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |
| LUVOCOM® 1105-7096 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |