| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 30gFyg_Halene-P-M315.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| M315 is a Heterophasic Polypropylene Impact Copolymer (PPiCP), produced by the latest generation Spheripol II Technology. This PPiCP is primarily suitable for Injection Molding process. It is recommended for use in injection molding processes where high flow and medium impact strength are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 6.0 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 1050 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 60 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 87.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 140 | °C | ASTM D1525 2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 210 | °C | |
| Middle Temperature | 180 to 210 | °C | |
| Front Temperature | 180 to 210 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M700R (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| Stanyl® 46HF5050 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| TOYOBO Urethane A1061D | TOYOBO America, Inc. | PUR-Butyl | TOYOBO Urethane |
| KOPLA PA6 KNR1031 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| Osterlene® PPC-12-1-C | Osterman & Company | PP Random Copolymer | Osterlene® |