TechnoFin PP MAGF
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | TechnoCompound GmbH |
| Trademark: | TechnoFin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2yZ7ta_TechnoFinPPMAGF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ranging from commodity to tailor-made compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.10 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 91.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 42.0 | MPa | ISO 527-2/50 |
| Fracture | 41.9 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 1.4 | % | ISO 527-2/50 |
| Fracture | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 9020 | MPa | ISO 178 |
| Flexural Stress 2 | 70.3 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 2.5 | kJ/m² | ISO 179/1eA |
| 23°C | 2.9 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 7.6 | kJ/m² | ISO 179/1eU |
| 23°C | 13 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 152 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 120 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 | ohms | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 6594B-G80E-A | TSRC Corporation | SEBS | T-Blend® |
| Hifax CA 1110 A2 | LyondellBasell Industries | PP Copolymer | Hifax |
| KumhoSunny PC/ABS HAC8250Z | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| KOPHOS® KO1365H | Kolon Plastics, Inc. | PC | KOPHOS® |
| LNP™ LUBRILOY™ Z2000 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRILOY™ |