Order Products : sales@su-jiao.com
CONTINUUM™ DMDD-6620 NT 7
| Category: | HDPE , Bimodal Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | CONTINUUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2xSGTM_CONTINUUM-DMDD-6620-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
CONTINUUM™ DMDD-6620 NT 7 Bimodal High Density Polyethylene Resin is produced by UNIPOL™ II process technology. This resin is a high stiffness resin with superior top-load performance in conjunction with excellent environmental stress crack resistance. DMDD-6620 NT 7 is specifically designed for use in extrusion blow molding equipment, producing containers up to 20 gallons in size, which require superior top-load combined with excellent environmental stress crack resistance. This reason offers excellent processability with low plate out properties. This product is especially well suited for containers used to package household industrial chemicals (e.g. detergents, and fabric softeners), toiletries and cosmetics (e.g. shampoos, creams, lotions, etc.), health and food products.
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.956 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.28 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 27 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 10% Igepal, F50 | 220 | hr | ASTM D1693 |
| 50°C, 100% Igepal, F50 | > 1100 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 24.8 | MPa | ASTM D638 |
| Fracture | 29.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.7 | % | ASTM D638 |
| Fracture | 800 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1170 | MPa | ASTM D790B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 131 | °C | ASTM D1525 |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行模塑和测试。 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P26M | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| ACRYPET® IR G304 | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | ACRYPET® |
| Cellophane™ 320MF | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Crastin® S600F40 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Sylvin 8379-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |