SCHULABLEND® (ABS/PA) M/MK 6501
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + PA |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2xLdqZ_SCHULABLENDABSPAMMK6501.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS/PA6 blend, standard injection molding grade |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 11.0 | -- | cm³/10min | ISO 1133 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 85.0 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1700 | 900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 39.0 | 27.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.4 | 21 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 22 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 80 | 91 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 87.0 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 66.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 204 | -- | °C | ISO 306/A50 |
| -- | 120 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.5 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.0 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.5 mm | 650 | -- | °C | IEC 60695-2-12 |
| 3.0 mm | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 40 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ELITE™ 5860 | The Dow Chemical Company | EPE | ELITE™ |
| Hiprolon® 200 NN | Arkema | Nylon 1010 | Hiprolon® |
| Karina WHITE PVC COMPOUND 806-10/236-H-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 6248-80 Yellow 4177 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ RX85514 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |