Daplen EG066AI is an elastomer modified polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 47.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 1050 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.3 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1000 | MPa | ISO 178 |
| Flexural Stress | 25.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.5 | kJ/m² | ISO 179/1eA |
| -20°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 38 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| -20°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 38 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -20°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 81.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ISO 306/A |
| -- | 54.0 | °C | ISO 306/B |
| Melt Energy | 86.0 | kJ/kg | ISO 11357 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperatrue: 40 - 80 °CMass Temperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PURFLEX™ TPO D80-BK09 | Pier One Polymers, Inc. | TPE | PURFLEX™ |
| MTEGRITY™ PS General Purpose GS218WC | M. Holland Company | PS (GPPS) | MTEGRITY™ PS General Purpose |
| Xuchuan 2155/B-8290 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Desmoderm® TXC ENB-01 | Covestro - PUR | PUR-Ester | Desmoderm® |
| LNP™ LUBRILOY™ DF204 compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |