InnoClear™ OC-7086
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoClear™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2vBKXT_InnoClear-OC-7086.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OC-7086 is a water-clear, rigid polyurethane formulated for room temperature hand-batch or vacuum assisted casting methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. The unique chemistry allows for excellent optical clarity as well as U.V. protection. Mixed material can be cast into either tin or platinum silicone molds. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.10 | g/cm³ | |
| Hardener | 1.10 | g/cm³ | |
| Base Resin | 1.13 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2380 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 95.0 | °C | |
| 1.8 MPa, Unannealed | 91.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 59 Mix Ratio by Weight: 57 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 120 to 240 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.45 | Pa·s | |
| 25°C 2 | 0.65 | Pa·s | |
| 25°C 3 | 1.3 | Pa·s | |
| Curing Time 4 | 28 | hr | |
| Gel Time | 15 to 20 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ASTM D2240 | |
| Tensile Modulus | 1830 | MPa | ASTM D638 |
| Tensile Strength | 72.4 | MPa | ASTM D638 |
| Tensile Elongation at Break | 8.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 4 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polyester APET SP-4110 | Spartech Plastics | PET | Spartech |
| PermaStat® 2800-70A | RTP Company | TPO (POE) | PermaStat® |
| Petrothene® NA594081 | LyondellBasell Industries | LDPE | Petrothene® |
| GELOY™ XP4034 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |
| Durethan® BKV 40 000000 | LANXESS Corporation | Nylon 6 | Durethan® |