SUMIPEX® MG5
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2v5QmS_SUMIPEX-MG5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIPEX general-purpose grades can be classified into two basic categories; good flow and heat resistant types. Each grade is available in pellet form. Bead form is available for some grades |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.90 | g/cm³ | JIS K7112 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.0 | g/10 min | JIS K7210 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | JIS K7209 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 95 | JIS K7202 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 72.0 | MPa | JIS K7113 |
| Tensile Elongation (Break) | 10 | % | JIS K7113 |
| Flexural Modulus | 3200 | MPa | JIS K7203 |
| Flexural Strength | 115 | MPa | JIS K7203 |
| Flexural Rigidity | 7.0 | % | JIS K7203 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Voltage Resistance 2 | 20.0 | kV/min | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.4 | kJ/m² | JIS K7110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 3(1.8 MPa, Annealed) | 99.0 | °C | JIS K7207 |
| Vicat Softening Temperature | 107 | °C | JIS K7206 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | JIS K6911 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | JIS K6911 |
| Dielectric Constant | 3.10 | JIS K6911 | |
| Dissipation Factor | 0.040 | JIS K6911 | |
| Insulation Resistance | > 1.0E+15 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 30 | mm/min | ASTM D63 |
| Flame Rating (1.59 mm, All Colors) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | JIS K7105 | |
| Transmittance 4 | 93.0 | % | JIS K7105 |
| Haze | < 0.50 | % | JIS K7105 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 220 to 260 | °C | |
| Middle Temperature | 220 to 260 | °C | |
| Front Temperature | 220 to 260 | °C | |
| Mold Temperature | 60.0 to 85.0 | °C | |
| Injection Pressure | 78.5 to 137 | MPa |
| Note Message | |
|---|---|
| 1 . | Method A |
| 2 . | 60%, 1kHz |
| 3 . | VST 25±3, 4 hrs |
| 4 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 236Q33 | SAX Polymers | Nylon 66 | SAXAMID™ |
| SHIN-A SEN-270A70 | SHIN-A T&C | Epoxy | SHIN-A |
| Tenopom® POM B3 G25 NTLA010 PR316 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| CELLIFF® 7000 | Microcell Composite Company | SBS | CELLIFF® |
| LNP™ LUBRILOY™ DF2041 compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |