XYLEX™ X8303 resin
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XYLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2ug18y_XYLEX-X8303-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC+ POLYESTER, Transparent, Low processing Temperature, High flow with excellent impact, UV stabilized. For In Mold Decoration /Labeling. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 27.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1680 | MPa | ASTM D638 |
| -- | 1690 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 46.0 | MPa | ASTM D638 |
| Yield | 48.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 44.0 | MPa | ASTM D638 |
| Fracture | 43.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 140 | % | ASTM D638 |
| Fracture | 140 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 1620 | MPa | ASTM D790 |
| -- 7 | 1720 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 72.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 72.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 1000 | J/m | ASTM D256 |
| -30°C 10 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 20 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 65.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 92.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 90.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ASTM D1525 13 |
| -- | 100 | °C | ISO 306/B50, ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 9.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 9.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 60°C | 9.8E-5 | cm/cm/°C | ISO 11359-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 235 - 255 | °C | |
| Middle Temperature | 235 - 265 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Nozzle Temperature | 240 - 270 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Screw Speed | 20 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL GTX™ GTX678 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| Detectaseal® XE7H | Precision Polymer Engineering Ltd. | EPDM | Detectaseal® |
| Geon™ Vinyl Rigid Extrusion 87150 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| G-Lene E36A060 | Gas Authority of India Limited | LLDPE | G-Lene |
| EPO-TEK® B9101-2 Unfilled | Epoxy Technology Inc. | Epoxy | EPO-TEK® |