Akulon® F-X9215
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2sgH7U_Akulon-F-X9215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Akulon® F-X9215 is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific. Primary attribute of Akulon® F-X9215: Medium Viscosity. |
| General Information | |
|---|---|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % | |
| Viscosity Number | 162 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 60.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 8.0 | -- | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | -- | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 9.0E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 275 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLARENE G181 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| Toraycon® EC44G-15 | Toray Resin Company | PBT | Toraycon® |
| UNITAL® Lf13 | Nytef Plastics, Ltd. | Acetal (POM) Homopolymer | UNITAL® |
| Daelim Po1y庐 LD-08 | DAELIM INDUSTRIAL CO., LTD. | LDPE | Daelim Po1y® |
| Hifax TYC 459X BLACK | LyondellBasell Industries | PP Copolymer | Hifax |