POTICON NT863

Category:	Nylon, Unspecified , Polyamide
Manufacturer:	Otsuka Chemical Co., Ltd.
Trademark:	POTICON
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2sVBFq_POTICONNT863.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

The Poticon series features a potassium titanate micro-filler compounded in thermoplastic resins to provide outstanding micro-reinforcement and dimensional stability. The excellent surface smoothness of these compounds limits friction toward opposing materials, reducing wear and allowing for greaseless applications. Moreover, as Poticon diminishes damage toward the mold and metal die and offers excellent recyclability, it also decreases processing costs.

Advantages

Microscopic reinforcement

Superior friction sliding and wear reduction

Excellent dimensional accuracy and surface smoothness

Highly recyclable

Applications

Automotive Parts (gears, bearings)

LED Reflectors

Watch Parts (gears, ground plane)

Camera (image stabilization parts)

Sliding Parts (gears, wheel bearing)

Camera Module Parts

Motor Parts (cog-wheels, bearings)

NT863 Property: High strength, Slide, Burning resistance

General Information
Features	High Dimensional Stability Low friction coefficient High strength Recyclable materials
Uses	LEDs Gear Application in Automobile Field Camera application Bearing
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.42	g/cm³	ASTM D792
Molding Shrinkage
Flow	0.90	%
Transverse flow	1.9	%
Water Absorption (Equilibrium)	0.18	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	110		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	143	MPa	ASTM D638
Tensile Elongation (Break)	4.0	%	ASTM D638
Flexural Modulus	8300	MPa	ASTM D790
Flexural Strength	224	MPa	ASTM D790
Coefficient of Friction (vs. Steel - Dynamic)	0.14
Abrasion Loss
-- ¹	3.80	10^-3 mm³/N·km
of counterpart ²	0.00	10^-3 mm³/N·km

Thermal	Nominal Value	Unit	Test Method
Heat Distortion	260	°C	ASTM D648

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	40	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow	2.1E-5	cm/cm/°C	ASTM D696

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Injection	Nominal Value	Unit
Processing (Melt) Temp	310 - 330	°C
Mold Temperature	120 - 140	°C
Injection Pressure	50.0 - 100	MPa

Note Message
1 .	Surface pressure: 1MPa
2 .	Slipping velocity: 0.3m/sec

Resin Grade	Manufacturer	Category	Trademark
POWERSIL® XLR® 640 A/B	Wacker Chemie AG	Silicone	POWERSIL®
Vyncolit® 1908K	Vyncolit N.V.	Epoxy	Vyncolit®
Clariant Nylon 6 PA-212	Clariant Corporation	Nylon 6	Clariant Nylon 6
Chiao Fu PA66/6 MB212G33 NAT	Chiao Fu Enterprises Co., Ltd.	Nylon 66/6	Chiao Fu PA66/6
Diamond ASA S130	Network Polymers, Inc.	ASA	Diamond ASA