NYCOA Polyamide 1047
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2rygsF_NYCOA-Polyamide-1047.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 1047 is a general purpose, heat stabilized Nylon 6 resin suitable for injection molding and extrusion applications. It is recommended for applications that require continuous exposure to temperatures in excess of 110° C. It features outstanding proc NYCOA 1047 is approved to numerous automotive specifications. It is recognized by Underwriters Laboratories for thicknesses as low as 0.7mm. It is listed as UL 94V-2. NYCOA 1047 is used for a variety of applications that include electrical connectors, gears, and convoluted tubing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.2 | % | ASTM D955 |
| Transverse flow | 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 90.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 3 | 2800 | MPa | ASTM D790 |
| Flexural Strength 4 | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 191 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.0 | °C | ASTM D648 |
| Continuous Use Temperature | 110 | °C | ASTM D794 |
| Melting Temperature | 221 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.700 mm) | V-2 | UL 94 |
| Additional Information |
|---|
| The value listed as Max. Continuous Use Tmp, ASTM D794 may not have been tested according to this standard. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 221 - 241 | °C | |
| Middle Temperature | 235 - 252 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 254 - 266 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS VP-3 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Sylvin 2902-80 Clear 8346 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen HP301R | LyondellBasell Industries | PP Homopolymer | Moplen |
| DIGITALWAX® RD 096 | DWS Systems | Unspecified | DIGITALWAX® |
| Ferro PP TPP30AN80BK | Ferro Corporation | PP, Unspecified | Ferro PP |