DOW™ HDPE 35060A
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2rq233_DOW-HDPE-35060A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW™ HDPE 35060A is a High Density Polyethylene resin produced in the Slurry Process. This resin presents good impact and environmental stress cracking resistance. Its high density allows reducing the weight of the container while maintaining good rigidity. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.961 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.29 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 27 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, molded) | > 200 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1.90mm, molded) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 1.90mm, molded | 29.0 | MPa | ASTM D638 |
| Fracture, 1.90mm, molded | 33.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 1000 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 1400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 42 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Additional Information |
|---|
| Recommended processing conditions: Temperature of the Cylinder: 180-190°C Temperature of the Die: 200°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® HP 2000 BK | Plastic Solutions, Inc. | PP Homopolymer | PrimaFlex® |
| Shinko-Lac® ASA TW30 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| TOTAL Polypropylene PPC 3660 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| HOPELEX PC-1150UR | Lotte Chemical Corporation | PC | HOPELEX |
| POLYCOMPO PP J226E | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |