Arak LLDPE LL0220CA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Shazand (Arak) Petrochemical Corporation |
| Trademark: | Arak LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2rEuRh_Arak-LLDPE-LL0220CA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL0220CA is a linear low density polyethylene copolymer containing butene-1 as a co-monomer. LL0220CA is suitable for production of cast stretch films. It can also be used as a blending partner in LDPE or LLDPE in both cast and blown film applications. The main characteristic of this grade is high TD tear strength that appropriates it for stretch applications. LL0220CA also can be used as compounds for low voltage power cable insulation or fibre optic jacketing. LL0220CA should be processed in machinery designed for LLDPE. Melt temperature range in the cast process are normally 240°C-280°C and in lean blends for blown film are 165°C-215°C. LL0220CA should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight. * LL0220CA is suitable for food contact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 to 0.920 | g/cm³ | ASTM D2838 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 to 2.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 28 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 8.00 | MPa | |
| TD : Yield | 7.50 | MPa | |
| MD : Break | 30.0 | MPa | |
| TD : Break | 20.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 480 | % | |
| TD : Break | 700 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 70 | g | |
| TD : 25 µm | 480 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 90 | ASTM D2457 | |
| Haze | 1.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blown Film Melt Temperature | 165 to 215 | °C | |
| Cast Film Melt Temperature | 240 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 MS | RTP Company | Nylon 66 | RTP |
| Maxxam™ FR QD 818.Y001 | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| RTP 6091 B-60A BLACK | RTP Company | TPV | RTP |
| 4DUR® 9K22130 HFR1 | 4Plas | PBT | 4DUR® |
| Evoprene™ LF 6158 | AlphaGary | SBC | Evoprene™ LF |