Chemlon® 240 G
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2rDZcY_Chemlon-240-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Chemlon® 240 G is a Polyamide 6 (Nylon 6) material filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Chemlon® 240 G: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 to 0.35 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 183 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.5 | % | |
| Break | 2.5 | % | |
| Flexural Modulus | 9650 | MPa | ASTM D790 |
| Flexural Strength | 262 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 207 | °C | ASTM D648 |
| Melting Temperature | 216 | °C | DSC |
| CLTE - Flow | 5.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 11 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 500 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | HB | UL 94 | |
| Oxygen Index | 22 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 218 to 235 | °C | |
| Middle Temperature | 252 to 257 | °C | |
| Front Temperature | 252 to 271 | °C | |
| Nozzle Temperature | 252 to 271 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 4538A | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |
| HONES® PA66 GF30 | Guangdong Shunde Hones Polymer Material Co., Ltd. | Nylon 66 | HONES® |
| INLUBE PPGF20TF15HSFC | Infinity LTL Engineered Compounds | PP, Unspecified | INLUBE |
| Karina COMP. PVC BLACK -E KAPU 6048/ 1D | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® LP510300 | LyondellBasell Industries | HDPE Copolymer | Petrothene® |