Xuchuan 1006A/B-5009
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Xuchuan Chemical (Suzhou) Co., Ltd |
| Trademark: | Xuchuan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2qPe3h_Xuchuan-1006A-B-5009.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Xuchuan 1006A/B-5009 is a Thermoplastic Polyurethane Elastomer (Polyether) (TPU-Polyether) product. It is available in Asia Pacific. Primary characteristic: good weather resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.450 to 0.650 | g/cm³ | |
| Density | |||
| A-1006A : 40°C | 1.010 to 1.020 | g/cm³ | |
| B-5009 : 40°C | 1.080 to 1.200 | g/cm³ | |
| Viscosity | |||
| A-1006A : 40°C | 400 to 800 | mPa·s | |
| B-5009 : 40°C | 300 to 600 | mPa·s |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Akron Abrasion | 0.0500 to 0.100 | cm³/1.61 km |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time | 8.0 to 10.0 | sec | |
| End of Rise Time | 1.0 to 1.2 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Free Rise Foam Density | 200 to 320 | kg/m³ | |
| Hydrolysis Strength Retention (70°C) 1 | > 95 | % | |
| Preheat Temperature | |||
| Part A | 50 to 60 | °C | |
| Part B | 60 to 70 | °C | |
| Preheat Time | |||
| Part A | 2.0 to 4.0 | hr | |
| Part B | 10.0 to 15.0 | hr | |
| Processing Temperature | |||
| Part A | 30 to 35 | °C | |
| Part B | 35 to 40 | °C | |
| Resilience | 30 to 40 | % |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 60 to 80 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 3.50 to 5.00 | MPa | |
| Tensile Elongation (Break) | 300 to 400 | % | |
| Tear Strength | 15.0 to 20.0 | kN/m |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 110 | ||
| Demold Time | 7.0 to 9.0 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 35.0 to 45.0 | °C |
| Note Message | |
|---|---|
| 1 . | 168 hr, 95% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209 TFE 5 | RTP Company | Nylon 66 | RTP |
| DOW™ HDPE DMDA-8810 NT 7 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Chemiton GTB5FA 80E | Franplast S.r.l. | SEBS | Chemiton |
| LNP™ STAT-KON™ DD0009XP compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| PLANAC BT-2200-60 | TOYOBO America, Inc. | PBT | PLANAC |