Ultradur® B 4406 G4
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2q8yz6_Ultradur-B-4406-G4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultradur B 4406 G4 is an injection molding grade with 20 % glass fibers for parts requiring enhanced fire resistance (eg relay housings, plug-and-socket connectors, switches, lighting components). Applications Typical applications include relay housings, plug-and-socket connectors, switches, and lighting components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | |
| Water Absorption | |||
| Saturation | 0.40 | % | ASTM D570 |
| Saturation, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 112.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Break, 23°C | 117 | MPa | ASTM D638 |
| Break, 23°C | 125 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break, 23°C | 2.2 | % | ASTM D638 |
| Break, 23°C | 2.6 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 48 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 215 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 223 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 177 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Peak Melting Temperature | 223 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | |||
| -- | 3.0E-5 | cm/cm/°C | ASTM E831 |
| -- | 5.0E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 0.750 mm | 140 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C | |
| RTI Imp | UL 746 | ||
| 0.750 mm | 120 | °C | |
| 1.50 mm | 120 | °C | |
| 3.00 mm | 120 | °C | |
| RTI Str | UL 746 | ||
| 0.750 mm | 125 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 1.50 mm | > 1.0E+15 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.60 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 7.0E-3 | ||
| 1 MHz | 0.017 | ||
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | < 1.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solprene® 303 | Dynasol Elastomers | SBR, Solution | Solprene® |
| APEX® 3703-80NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Gallonprene® GP520-4505 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Jamplast EX-03 | Jamplast, Inc. | PVC, Unspecified | Jamplast |
| Karina NATURAL PVC COMPOUND 752-25/ 1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |